Carrier 37610 Hi-Temp Silicone

Carrier 37610 Replacement Part

Note: WARNING: Eye & Skin Irritant

Includes:

• (1) - Hi-Temp Silicone (37610)

Specifications

• BOSS376 HVAC/R High Temp Red Silicone Sealant
• 10.1 Oz (300 ml)
• FEATURES:
• Sealing and encapsulating heating elements in appliances
• Stove and furnace vent pipes
• Moving oven belts
• Industrial ovens
• Bag filters on smoke stacks
• Other critical bonding, sealing, potting, encapsulating and protective coating where parts must perform at high temps
• Typical Properties:
• Color: Red
• Flow/Slump: NIL
• Extrusion Rate (1/8" orifice, 90 PSI): 335 Gal/Min
• Cure Characteristics - Exposed to Air, 77 Degrees Fahrenheit (25C) and 50% RH
• Skin-over Time: 5-8 Minutes
• Tack-free Time: 20 Minutes
• Cure Time (1/8" thickness): 24 Hours
• As Cured - After 72 Hours at 77 Degrees Fahrenheit (25C) and 50RH
• Durometer, Shore A: 30 Points
• Tensile Strength: 325 PSI
• Elongation: 475%
• Unprimed adhesion (most substrates*): Good
• Special Properties:
• Performs at Temperatures Ranging from -85 Degrees Fahrenheit to 500 Degrees Fahrenheit (-65C to 260C) *
• Optimum adhesion is obtained in 7-10 days curing time.
• Use A-120 prime coat if increased adhesion is required.

Replaces Old Carrier Part Numbers

• There are no older part numbers.

Other Part Numbers

Hi-Temp Red Silicone was formulated to perform at temperatures ranging from -85 degrees Fahrenheit to 500 degrees Fahrenheit (-65 degrees to 260 degrees Celsius) for continuous operation . These features make BOSS 376 ideal for use around heat exchangers, restaurant hoods and furnace vent pipes., DIRECTIONS:, 1. Clean and dry surface. Remove any soap, oil or grease., 2. Cut tip off cartridge just above threads. Screw on nozzle and cut on 45 degree angle to desired bead size. Insert Cartridge into standard caulking gun., 3. For a smooth seal, hold at 45 degree angle and apply by pushing sealant ahead of nozzle., 4. Tooling must be completed in 5 minutes. Remove excess with dry paper towel., 5. Normally sealant "skins" in 5 minutes, dries to touch in 1 hour, and cures and bonds in 24 hours. Optimum strength is achieved in 7 days., 6. After sealant is completely cured, excess material can be removed by trimming with a sharp blade. Avoid undercutting seal., 7. RESEALABLE: If entire contents are not used, extrude 3/8" of sealant beyond nozzle opening. When ready to reuse, pull out cured plug. ENTIRE CONTENTS SHOULD BE USED WITHIN 12 MONTHS., SPECIFICATIONS:, NSF Standard 51. UL Recognized. Meets Specification for Federal Meat and Poultry Inspection Problem: FDA Regulation no. 21 CFR 177.2600 and Federal Specifications TT-S-001543A, TT-S-00230C and ASTM C920-86., CAUTION, DIRECT CONTACT OF UNCURED SEALANT IRRITATES EYES AND MAY IRRITATE SKIN. OVEREXPOSURE VAPOR MAY IRRITATE EYES, NOSE AND THROAT. Avoid eye and skin contact. Use with adequate ventiulation. Do not handle contact lenses with sealant on hands. IN CASE OF EYE CONTACT, flush eyes with water fir 15 minutes. Obtain medical attention. IN CASE OF SKIN CONTACT, remove from skin and flush with water. Sealant releases acetic avid (vinegar-like odor) during cure. KEEP OUT OF REACH OF CHILDREN. FOR INDUSTRIAL USE ONLY., Non-warranty: Because the storage, handling and application of the material is beyond our control, Accumetric accepts no liability for the results obtained. Accumetric's sole limited warranty is the product meets the manufacturing specifications in effect at time of shipment. The exclusive remedy for breach of such limited warranty is a refund of purchase price or replace ent of any product shown to be other than as warranted., Reactive VOC 28 g/l (<3% wt), Item No. 37610, Net 280ml, MADE IN U.S.A., BOSS Products, Accumetric, LLC, Elizabethtown, KY 42701, 800-928-BOSS(2677), 270-769-3385 FAX 270-765-2412, www.bossproducts.com, 787930376107, 151077321, NSF/FDA Compliant, U.S. GREEN BUILDING COUNCIL MEMBER